TEST
DESCRIPTION
|
METHOD
|
UNIT
|
RESULTS
|
| Resin
Content |
-
|
%(by
weight)
|
70%
Resin (± 5%)
|
| Fibre
Volume Fraction |
-
|
%(by
weight)
|
30%
E Glass (± 5%)
|
| Width
Finished Product |
AS
2001.2.12
|
mm
|
1270
±1%
|
| Weight
Finished Product |
AS
2001.2.13
|
g/m2
|
2290
± 5%
|
Flexural
Strength
(8ply - 7.9mm thickness) |
ASTM
D790
|
MPa
|
Warp:
290 ± 40
|
Weft:
175 ± 50
|
Flexural
Modulus
(8 ply - 7.9mm thickness) |
ASTM
D790
|
GPa
|
Warp:
9 ± 1
|
Weft:
5 ± 0
|
Tensile
Strength
(2 ply - 1.8mm thickness) |
ASTM
D2344M
|
MPa
|
Warp:
120 ± 15
|
Weft:
110 ± 15
|
Tensile
Modulus
(2 ply - 1.8mm thickness) |
ASTM
D3039M
|
MPa
|
Warp:
7.3 ± 0.3
|
Weft:
7.7 ± 0.3
|
Interlaminar
Shear Strength
(8 ply - 7.9mm thickness) |
ASTM
D3039M
|
GPa
|
Warp:
18 ± 1
|
Weft:
18 ± 1
|