TEST
DESCRIPTION
|
METHOD
|
UNIT
|
RESULTS
|
| Resin
Content |
-
|
%
|
80%
Resin (± 5%)
|
| Fibre
Volume Fraction |
-
|
%
|
20%
C Veil
|
| Width
Finished Product |
AS
2001.2.12
|
mm
|
1000
±1%
|
| Weight
Finished Product |
AS
2001.2.13
|
g/m2
|
580
± 5%
|
Flexural
Strength
(8ply - 7.9mm thickness) |
ASTM
D790
|
MPa
|
Warp:
130 ± 4
|
Weft:
130 ± 4
|
Flexural
Modulus
(8 ply - 7.9mm thickness) |
ASTM
D790
|
GPa
|
Warp:
4.3 ± 0.2
|
Weft:
4.6 ± 0.7
|
Tensile
Strength
(2 ply - 1.8mm thickness) |
ASTM
D2344M
|
MPa
|
Warp:
60 ± 4.7
|
Weft:
63 ± 3.6
|
Tensile
Modulus
(2 ply - 1.8mm thickness) |
ASTM
D3039M
|
MPa
|
Warp:
3.6 ± 0.2
|
Weft:
3.7 ± 0.2
|
Interlaminar
Shear Strength
(8 ply - 7.9mm thickness) |
ASTM
D3039M
|
GPa
|
Warp:
23.0 ± 1.1
|
Weft:
23.0 ± 1.1
|