TEST
DESCRIPTION
|
METHOD
|
UNIT
|
RESULTS
|
| Resin
Content |
-
|
%(by
weight)
|
50
% ± 5%
|
| Fibre
Volume Fraction |
-
|
%(by
weight)
|
50
% ± 5%
|
| Width
Finished Product |
AS
2001.2.12
|
mm
|
1270
±1%
|
| Weight
Finished Product |
AS
2001.2.13
|
g/m2
|
1750
±5%
|
Flexural
Strength
(8ply - 7.9mm thickness) |
ASTM
D790
|
MPa
|
Warp:
140 ± 4
|
±
45°: 581 ± 8
|
Weft:
151 ± 5
|
Flexural
Modulus
(8 ply - 7.9mm thickness) |
ASTM
D790
|
GPa
|
Warp:
10.1 ± 0.3
|
±
45°: 25.2 ± 0.5
|
Weft:
11.7 ± 0.5
|
Tensile
Strength
(2 ply - 1.8mm thickness) |
ASTM
D3039M
|
MPa
|
Warp:
81 ± 3
|
±
45°: 315 ± 18
|
Weft:
82 ± 6
|
Tensile
Modulus
(2 ply - 1.8mm thickness) |
ASTM
D3039M
|
GPa
|
Warp:
18.0 ± 0.2
|
±
45°: 28.0 ± 0.6
|
Weft:
18.0 ± 0.2
|
Interlaminar
Shear Strength
(8 ply - 7.9mm thickness) |
ASTM
D2344
|
MPa
|
Warp:
38.0 ± 0.8
|
±
45°: 38.0 ± 0.8
|
Weft:
38.0 ± 0.8
|