TECHNICAL SPECIFICATIONS
MATERIAL / FORM	IMPREGNATED GLASS FABRIC
COLOR	WHITE
APPLICATION METHOD	WATER-ACTIVATED WET LAY-UP
NUMBER OF PILES REQUIRED	10 MINIMUM
THICKNESS	11± 2 MILS
RESIN CONTENT	35% NOMINAL
WORKING TIME	60 MINUTES, DEPENDING ON THE AMBIENT HUMIDITY
CURE CYCLE 75°F (24°C)	30 MINUTES NOMINAL
HARDNESS-CURED LAMINATE	85 SHORE D NOMINAL
DIELECTRIC STRENGTH	NON-CONDUCTIVE WHEN CURED/ 16,000 VOLTS
HEAT RESISTANCE (24-HOUR CURE)	400°F MAX (204°C)
MAXIMUM INSTALLATION TEMPERATURE	200°F (93°C)
TAPE WIDTH	2",3",4",6" AND 10"
ROLL LENGTH	5’ TO 150’ DEPENDING ON WIDTH
TOXICITY	CONTAINS NO HARMFUL SOLVENTS AND CAN BE USED ON WATER AND FOOD SERVICE LINES
DOT-NON-HAZARDOUS	FREIGHT CLASS NO1-ITEM 4620 SUB 5 CLASS 60
SHELF LIFE	12 MONTHS IN ITS ORIGINAL PACKAGE. STORE IN A CLEAN DRY PLACE AND DO NOT REFRIGERATE
(SOME SOFTENING) AND OTHER FLUIDS	ETHYL ALCOHOL, HCl
LOAD PER PLY PER INCH OF WIDTH	650 POUNDS
FOR 1% ELONGATION	380 POUNDS
THERMAL EXPOSURE EFFECT	25% SOFTENING AT 245°C

MECHANICAL PROPERTIES
		FRP	CARBON
Structure	Method	PSI/Temp	PSI/Temp
TENSILE STRENGTH 75°F(24°C)	ASTM D 3039	65, 000	123, 000
TENSILE MODULUS 75°F (24°C)	ASTM D 3039	3.8 X 10^6	11.4 X 10^6
FLEXURAL STRENGTH 75°F (24°C)	ASTM D 790	26, 300	35, 000
FLEXURAL MODULUS 75°F (24°C)	ASTM D 790	1.65 X 10^6	2.85 X 10^6
COMPRESSION STRENGTH	ASTM D 695	12, 820	20, 000
INTERLAMINAR SHEAR @ 75°F (24°C)	ASTM D 2344	3, 850	2, 800
Tg (GLASS TRANSITION TEMPERATURE)	ASTM E 831	287.6°F (142°C)	122°C

CHEMICAL RESISTANCE TEST – ASTM D 831 (A)
Chemical	Result
ACETONE	PASS
DIESEL FUEL	PASS
ETHYL ALCOHOL	SOME SOFTENING
GASOLINE	PASS
30 % HCL	SOME SOFTENING
MEK	PASS
TOLUENE	PASS
NOTE: THE CURED WRAP IS A WOVEN E. GLASS FIBERMAT / URETHANE COMPOSITE SLEEVE & THE LIFE AT AMBIENT TEMPERATURES 30 – 40°CSHOULD BE MORE THAN 50 YEARS.